Modified Nylon Plastic Raw Material PA6 GF30 V0 Granules

Modified Nylon plastic raw material PA6 GF30 V0 granules required to have high strength and high heat resistance. The PA6-GF30 products are stable at high temperatures, have good mechanical properties, and are lightweight. pa6-gf25 are widely used in automotive engine parts, electrical parts, body parts and airbags. While maintaining the aesthetics of the vehicle, it is recognized by major automobile manufacturers.The actual shrinkage is also a function of the plastic part design, wall thickness and other process parameters.

Send Inquiry Now

Download Instruction

Our Product Detail

Description of this Modified Nylon Plastic Raw Material PA6 GF30 V0 Granules
 
Modified Nylon plastic raw material PA6 GF30 V0 granules required to have high strength and high heat resistance. The PA6-GF30 products are stable at high temperatures, have good mechanical properties, and are lightweight. pa6-gf25 are widely used in automotive engine parts, electrical parts, body parts and airbags. While maintaining the aesthetics of the vehicle, it is recognized by major automobile manufacturers.The actual shrinkage is also a function of the plastic part design, wall thickness and other process parameters.

Modified Nylon plastic raw material PA6 GF30 V0 granules, it is recommended that the mold temperature be 80 to 90 °C. For thin-walled, longer-flowing parts, it is also recommended to apply higher mold temperatures. Increasing the mold temperature increases the strength and stiffness of the part, but reduces the toughness. If the wall thickness is greater than 3mm, it is recommended to use a low temperature mold of 20~40 °C. For glass reinforcement the mold temperature should be greater than 80C.

Parameters of this Modified Nylon Plastic Raw Material PA6 GF30 V0 Granules
 

Item

Standard

Unit

PA6-5801

Density

GB/T 1033-2008

g/ cm3

1.23

Melt flow rate ( 230°C,2.16kg)

GB/T 3682-2000

g/ 10min

/

Tensile strength

GB/T 1040-2006

MPa

75.78

Breaking elongation

GB/T 1040-2006

%

10

Blending strength

GB/T 9341-2008

MPa

130.9

bendingmodulus

GB/T 9341-2008

MPa

3450

Heat distortation temperature

( 0.45 MPa)

 

GB/T 1634-2004

°C

90

NIIS( 23 °C)

GB/T 1843-2008

KJ/ m2

3.5

Flame retardant grade

UL-94

/

V-0

 
Pictures of this Modified Nylon Plastic Raw Material PA6 GF30 V0 Granules
 
 
 
FAQ of this Modified Nylon Plastic Raw Material PA6 GF30 V0 Granules
 
 
Certificate of this Modified Nylon Plastic Raw Material PA6 GF30 V0 Granules
 
Company of this Modified Nylon Plastic Raw Material PA6 GF30 V0 Granules
 
 
 
Looking forward to your inquiry for this Modified Nylon Plastic Raw Material PA6 GF30 V0 Granules

You might also like

Leave A Message