Modified Nylon Plastic Raw Material PA6 GF30 V0 Granules

 

We are a professional manufacturer and exporter of Modified Nylon Plastic Raw Material PA6 GF30 V0 Granules in China. We accept customization and OEM of modified material. Modified Nylon plastic raw material PA6 GF30 V0 granules required to have high strength and high heat resistance. The PA6-GF30 products are stable at high temperatures, have good mechanical properties, and are lightweight. pa6-gf25 are widely used in automotive engine parts, electrical parts, body parts and airbags. While maintaining the aesthetics of the vehicle, it is recognized by major automobile manufacturers.The actual shrinkage is also a function of the plastic part design, wall thickness and other process parameters.

Modified Nylon plastic raw material PA6 GF30 V0 granules, it is recommended that the mold temperature be 80 to 90 °C. For thin-walled, longer-flowing parts, it is also recommended to apply higher mold temperatures. Increasing the mold temperature increases the strength and stiffness of the part, but reduces the toughness. If the wall thickness is greater than 3mm, it is recommended to use a low temperature mold of 20~40 °C. For glass reinforcement the mold temperature should be greater than 80C.

 

Item	Standard	Unit	PA6-5801
Density	GB/T 1033-2008	g/ cm3	1.23
Melt flow rate ( 230°C,2.16kg)	GB/T 3682-2000	g/ 10min	/
Tensile strength	GB/T 1040-2006	MPa	75.78
Breaking elongation	GB/T 1040-2006	%	10
Blending strength	GB/T 9341-2008	MPa	130.9
bendingmodulus	GB/T 9341-2008	MPa	3450
Heat distortation temperature ( 0.45 MPa)	GB/T 1634-2004	°C	90
NIIS( 23 °C)	GB/T 1843-2008	KJ/ m2	3.5
Flame retardant grade	UL-94	/	V-0