PA66 Nylon 6 Nylon 66 Granule Polyamide 66 PA Granule for Modified Engineering

PA66 / Nylon 6 / Nylon 66 Granule /Polyamide 66 PA granule for modified engineering has stable quality of product, uniform relative molecular weight . Superior electrical insulation property, Alkali resistance, abrasion resistance and corrosion resistance. It is mainly applied to Nylon short silk which short fiber can be blended with cotton, wool and viscose fiber, containing good abrasive resistance and strength. It also can be used for loop fasteners, decorative cloth, etc. Products like tyre fabrics, band carrier, fishing net and mooring rope are made by PA6 bright chips in industry.

details

Description of this PA66 Nylon 6 Nylon 66 Granule Polyamide 66 PA Granule for Modified Engineering
 
PA66 / Nylon 6 / Nylon 66 Granule /Polyamide 66 PA granule for modified engineering has stable quality of product, uniform relative molecular weight . Superior electrical insulation property, Alkali r

esistance, abrasion resistance and corrosion resistance. It is mainly applied to Nylon short silk which short fiber can be blended with cotton, wool and viscose fiber, containing good abrasive resista

nce and strength. It also can be used for loop fasteners, decorative cloth, etc. Products like tyre fabrics, band carrier, fishing net and mooring rope are made by PA6 bright chips in industry.PA66 / Nylon 6 / Nylon 66 Granule /Polyamide 66 PA granule for modified engineering is white or slightly yellow transparent to opaque horny-like crystalline polymer, free coloring, toughness, wear res
 

istance, self-lubricating, low rigidity, low temperature resistance, bacteria can slow burn from the fire slowly put out there dripping, blistering, excellent in moldability: injection molding, blow m

olding, pour molding, spraying, powder molding, machining, welding, bonding.

Parameters of this

PA66 Nylon 6 Nylon 66 Granule Polyamide 66 PA Granule for Modified Engineering

Item

Standard

Unit

PA6-5801

Density

GB/T 1033-2008

g/ cm3

1.23

Melt flow rate ( 230°C,2.16kg)

GB/T 3682-2000

g/ 10min

/

Tensile strength

GB/T 1040-2006

MPa

75.78

Breaking elongation

GB/T 1040-2006

%

10

Blending strength

GB/T 9341-2008

MPa

130.9

 

Bending modulus

GB/T 9341-2008

 

 

 

MPa

 

 

3450

 

 

Heat distortation temperature

( 0.45 MPa)

GB/T 1634-2004

°C

90

NIIS( 23 °C)

GB/T 1843-2008

KJ/ m2

3.5

 
Flame retardant gradeUL-94
 
 

 

/V-0
 
 
Pictures of this PA66 Nylon 6 Nylon 66 Granule Polyamide 66 PA Granule for Modified Engineering
 
FAQ of this PA66 Nylon 6 Nylon 66 Granule Polyamide 66 PA Granule for Modified Engineering
 
 
 
Certificate of this PA66 Nylon 6 Nylon 66 Granule Polyamide 66 PA Granule for Modified Engineering